Jiangyin JiHua

Structure:

pbt-re1.jpg (3745 bytes)

Property：

- Good heat resistance (especially in melting point and distortiontemperature) so as to can be used at high temperature continuouslyand have long time heat stability;
- High mechanical strength、low friction coefficient and abrasion proof;
- Low moisture absorption so as to has less effect on mechanism and stability after saturation;
- PBT engineering plastics show inertia to the majority of chemicalmedicine except for hot water and alkali;
- Good fluidity and easy machine-shaping, short cycle time and excellent surface lubricity and lustre so as to can be made to wallthinness and complicated shape product;
- Include Ultra-resistance grade and can be used to special appliances;
- Flame retardance meeting the requirements of UL 94 standards (E139063).

Typical Application：

- Illuminate electric Power adapter stock and base of energy-saving light and lamps housing.

Use Method：

- Need to dry before injection molding, you can dry it at 120-130 ℃ for 4-5 hours (material thickness
not exceeding 3 cm).

Injection Molding Condiction as Follows (only to Perference)：

Item		Unit	Process coditions
Cylinder Temperature	Rear	℃	230-245
	Middle	℃	235-250
	Front	℃	240-250
Nozzle Temperature		℃	240-260
Material Temperature		℃	240-260
Mold Temperature		℃	50-100
Injection Pressure		kg/cm²	700-1200
Packing pressure		kg/cm²	400-850
Back Pressure		kg/cm²	0-40
Screw Speed		Rpm	40-75

Represented Value of PBT Resin According to ASTM as Follows：

Property			ASTM	Unit	4308 G0	4308 G10	4308 G15	4308 G20	4308 G30
Physical Property	Density		D792	g/cm³	1.50	1.52	1.54	1.56	1.60
	Water absorption /23℃505RH		D570	%	0.10	0.10	0.10	0.10	0.10
	Shrinkage		D955	%	2.0	0.8-1.9	0.7-1.7	0.6-1.5	0.4-1.1
Mechanical property	Tensile strength		D638	MPa	60	80	90	100	115
	Elongation at break		D638	%	15	4	3	3	2
	Flexural strength		D790	MPa	90	130	145	160	185
	Flexural modulus		D790	MPa	2500	3500	4500	6000	9000
	Izod impact strength	Notched	D256	J/m	35	50	55	60	70
	Izod impact strength	Un-notched	D256	J/m	200	250	300	350	450
Thermal property	HDT	1.82Mpa	D648	℃	60	185	190	200	205
	HDT	0.46MPa	D648	℃	150	200	210	215	220
	Combustibility (1/16”)		UL-94	__	V-0	V-0	V-0	V-0	V-0
Electrical property	Dielectric strength		D149	Kv/mm	21	21	21	21	21
	Volume resistivity		D257	Ω-mm	10¹⁶	10¹⁶	10¹⁶	10¹⁶	10¹⁶
	Dielectric constant (10⁶Hz)		D150	__	3.2	3.2	3.4	3.4	3.5
	Dielectric loss constant(10⁶Hz)		D150	__	0.02	0.02		0.02	0.02
Characteristics			__	___	Flame retardant grade	10% fibre rein forced	15% fibre rein forced	20% fibre rein forced	30% fibre rein forced

Packing and stockpile：

25KG plastic valve bag, storage in dry, well ventilated and keep out of sun.

BACK

Jiangyin JiHua New Material Co., Ltd.


PBT Resin	Gen. FlameR. PBT	Rein. & Tou.PBT	Saving Energy PBT	High Perf. PBT

				High Perf. PBT