ABS

Structure:

Property：

■ Not transparency 、good coloring property、can be colored to a product of good surface gloss easily.

■Excellent contra-impact property and not rapidly decline at low temperature.

■Electrical insulation seldom suffer from temperature and humidity ,and can keep constant at widely frequency variation range.

■Extra-impact strength will decline after exposed to the open air at long term basis ,bad weatherability and UV resistance.

Typical Application：

■Gear wheel 、impeller handle 、pipeline 、electrical machine housing、instrument panel 、refrigerator lining、storage sump、 inner liner、 style things and toy.

■Can be substituted for metal ,name-plate、 decoration parts .

■flame retarded ABS can be made to electronic housing and less high temperature parts .reinforce ABS can be made to axial current and centrifugalization leaf of air conditor.

Use Method：

■Need to pre-dry before injection molding , dry at80- 90℃ for1 -- 2 hours.

Injection Molding Condiction as Follows (only to Perference)：

Item		Unit	Unreinforced	Reinforced
Cylinder temperature	Rear	℃	180-190	190-200
	Middle	℃	190-210	200-220
	Front	℃	200-220	210-230
Nozzle temperature		℃	200-220	210-230
Resin temperature		℃	210-230	220-240
Mold temperature		℃	60-80	60-80
Injection pressure		kg/cm²	500-800	700-1000
Packing pressure		kg/cm²	600-750	800-900
Back pressure		kg/cm²	0-40	0-40
Screw speed		rpm	50-70	40-60

Represented Value of ABS Resin According to ASTM as Follows：

Property		ASTM	Unit	3700	6406	4400 G15	4400 G30	PC/ ABS	AS4400 G30
Physical Property	Density	D792	g/cm³	1.01	1.22	1.15	1.3	1.14	1.34
Physical Property	Shrinkage factor	D955	%	0.7-0.9	0.5-0.8	0.2-0.4	0.1-0.3	0.5-0.7	0.1-0.3
Mechanical property	Tensile strength	D638	MPa	0.7-0.9	0.5-0.8	0.2-0.4	0.1-0.3	0.5-0.7	0.1-0.3
	Flexural strength	D790	MPa	23	42	80	105	50	115
	Flexural modulus	D790	MPa	50	65	110	130	710	195
	Cantilever beam impact strength	D256	J/m	1700	2300	5000	9500	/	7000
Thermal property	H.D.T.1.82Mpa	D648	℃	400	170	80	60	62	56
Thermal property	Combustibility(1/16”)	UL-94	____	HB	V-0	HB	HB	HB	HB
Characteristics				Tough-ness	Flame retarded	Reinfor--ced 15%GF	Reinfor--ced 30%GF	PC,ABS Alloy	Reinfor--ced 30%GF

Packing and stockpile：

25KG plastic valve bag, storage in dry, well ventilated and keep out of sun.